吴冰青, 王文魁, 靳常青, 刘维, 李方华, 刘世超, 刘振兴, 赵忠贤, 姚玉书

QUASI-HYDROSTAT1CALLY COLD-PRESSED Bi0.8Pb0.2SrCaCu2Ox SUPERCONDUCTORS

WU BING-QING, WANG WEN-KUI, JIN CHANG-QING, LIU WEI, LI FANG-HUA, LIU SHI-CHAO, LIU ZHEN-XING, ZHAO ZHONG-XIAN, YAO YU-SHU
PDF
导出引用
  • 着重讨论了准静水冷压对Bi系高温超导材料超导电性的影响,并分析了经冷压-退火处理后超导电性的改善情况。准静水冷压处理后,Bi系超导材料晶粒间界连接发生显著退化,晶粒内部产生大量缺陷,由此导致了宏观超导电性的退化。冷压造成了体密度的极大提高和一定的晶粒择优取向。这些现象主要是由于准静水压下剪切应力的作用。退火后,晶界连接得到很大加强,部分缺陷消失或形成堆错使材料各项性能均获改善。Jc(77K,零场)较初始样品有大幅度提高,达约1600A/cm2。此外还考察了静水压
    The effects of quasi-hydrostatic pressure treatments on the Bi-system superconductors were investigated The cold-pressing treatments seriously weakened the inter-granular weaklinks and induced a large number of intragranular defects, resulting in the deterioration of the suprcon-ducting properties. The targe increase in the bulk density and the orientation of the superconducting grains were also observed in the cold-pressed samples. These drastic changes of superconductivity were mainly due to the shear stress under quasi-hydrostatic pressure. The post annealing treatments greatly enhanced the weaklinks and caused the partial recovery and the agglomeration of some defects. By coldpressing-annealing method, Jc (77 K, zero field) was raised to about 1600A/cm2. The pressure dependence of Tc under hydrostatic pressure was also investigated and dTc/dp was found to be 1.4K/GPa.
    计量
    • 文章访问数:7283
    • PDF下载量:1224
    • 被引次数:0
    出版历程
    • 收稿日期:1991-12-11
    • 刊出日期:1992-06-05

      返回文章
      返回