摘要

在钙钛矿电池中, ZnO纳米棒的垂直性是影响器件效率的关键因素. AZO(ZnO:Al)玻璃作为一种廉价的透明导电衬底, 由于与ZnO纳米棒无晶格失配, 有望获得最佳垂直性. 然而目前在大气环境下, 以AZO为衬底、ZnO纳米棒为电子传输层的钙钛矿太阳能电池还鲜有报道. 本文通过水热法制备ZnO纳米棒作为电子传输层, 系统研究不同条件对ZnO纳米棒的形貌及结晶性能的调控规律, 分析其微观生长机理. 并在此基础上于大气环境下制备太阳能电池, 将以AZO为衬底在大气条件下制备的钙钛矿光伏器件的最佳效率从目前文献报道的7.0%提高到9.63%. 这对丰富钙钛矿电池的设计思路及进一步降低成本具有重要意义.

关键词:

Abstract

ZnO is a promising electron transport material. It has not only similar energy level position and physical properties to traditional TiO ₂, but also excellent light transmittance, conductivity, stability, low cost and low temperature preparation. Studies have shown that the one-dimensional nanostructured electron transport layer has a higher electron transport rate, provides a direct electron transport channel and avoids its being recombined at the grain boundaries, thereby improving carrier collection efficiency. It has also been reported that the electron transport rate of ZnO nanorods is significantly better than that of TiO ₂, showing their great potential applications. In perovskite solar cells, the verticality of ZnO nanorods is a key factor affecting device efficiency. The AZO (ZnO∶Al) glass, as an inexpensive transparent conductive substrate, is expected to obtain the best verticality because it has no lattice mismatch with ZnO nanorods. And in the field of perovskite solar cells, the light absorbing layer is usually prepared in a glove box and it has obviously not been industralized. However, there are few reports about perovskite solar cells prepared in atmospheric environment with AZO as substrate and ZnO nanorods as electron transport layer. And it is still much less efficient than the current perovskite solar cells with TiO ₂as the electronic transport layer. It can be seen that further improving the efficiency of the structural battery prepared in the atmospheric environment is an urgent problem to be solved. In this paper, ZnO nanorods are prepared as an electron transport layer by the hydrothermal method. The effects of hydrothermal temperature, the number of seed layer, the precursor concentration, the substrate type, the hydrothermal time, and the other process parameters on the morphology and crystalline properties of ZnO nanorods are systematically studied, and the growth mechanism is analyzed. The results show that the length of the nanorods is mainly controlled by the hydrothermal time and hydrothermal temperature, and that the radial size is mainly determined by the number of seed layers and the concentration of the precursor solution. And the results also indicate that the verticality of ZnO nanorods’ growth is closely related to the substrate, and that the ZnO nanorods on the AZO substrate have the best growth verticality. On this basis, the perovskite solar cell is prepared in the atmospheric environment, and the optimal efficiency of the photovoltaic device prepared with AZO substrate increases from 7.0% reported in the literature to 9.63%. This is of great significance for enriching the design ideas of perovskite solar cells and further reducing costs.

Keywords:

作者及机构信息

通信作者:郝会颖,huiyinghaoL@cugb.edu.cn

Authors and contacts

Corresponding author:Hao Hui-Ying,huiyinghaoL@cugb.edu.cn

文章全文: translate this paragraph

参考文献

[1]
[2]
[3]
[4]
[5]
[6]
[7]
[8]
[9]
[10]
[11]
[12]
[13]
[14]
[15]
[16]
[17]
[18]
[19]
[20]

施引文献

下载: 全尺寸图片幻灯片

条件	温度/℃	平均直径/nm	平均长度/nm
1	50	28	47
2	60	33	245
3	70	30	550
4	80	31	740
5	90	34	948
6	100	32	871

下载: 导出CSV

条件	衬底	保温时间/h	平均长度/nm	平均直径/nm
1	AZO	1.5	132	76
2	AZO	2.5	244	92
3	AZO	3.5	503	139
4	AZO	5.0	620	121
5	AZO	6.0	722	189
6	AZO	7.0	701	136
7	AZO	8.0	866	204
8	AZO	9.0	470	135
9	AZO	10.0	255	94

下载: 导出CSV

水热条件/h	Scan directions	V_oc/V	J_sc/mA·cm^–2	FF	平均PCE/%	最佳PCE/%
2.5	Reverse	0.77	18.51	0.47	6.71	7.96
5.0	Reverse	0.84	20.99	0.48	8.47	9.63
8.0	Reverse	0.52	17.15	0.43	3.85	6.00

下载: 导出CSV

[1]
[2]
[3]
[4]
[5]
[6]
[7]
[8]
[9]
[10]
[11]
[12]
[13]
[14]
[15]
[16]
[17]
[18]
[19]
[20]

[1]	徐洁, 冯泽华, 刘冰野, 朱欣怡, 代锦飞, 董化, 吴朝新.聚合物内封装层辅助空气中钙钛矿模组器件制备及其光电特性. 必威体育下载 , 2023, 72(24): 248802.doi:10.7498/aps.72.20231055
[2]	羊美丽, 邹丽, 程佳杰, 王佳明, 江钰帆, 郝会颖, 邢杰, 刘昊, 樊振军, 董敬敬.聚偏氟乙烯添加剂提高CsPbBr₃钙钛矿太阳能电池性能. 必威体育下载 , 2023, 72(16): 168101.doi:10.7498/aps.72.20230636
[3]	隋国民, 严桂俊, 杨光, 张宝, 冯亚青.二维氟代苯甲胺钙钛矿结构和光电性能的理论研究. 必威体育下载 , 2022, 71(20): 208801.doi:10.7498/aps.71.20220802
[4]	孙盟杰, 何志群, 郑毅帆, 邵宇川.EDTA/SnO₂双层复合电子传输层在钙钛矿电池中的应用. 必威体育下载 , 2022, 71(13): 137201.doi:10.7498/aps.71.20220074
[5]	仲婷婷, 张晨, 哈木, 徐望舒, 唐坤鹏, 徐翔, 孙文天, 郝会颖, 董敬敬, 刘昊, 邢杰.采用PEABr添加剂获得高效且稳定的碳基CsPbBr₃太阳能电池. 必威体育下载 , 2022, 71(2): 028101.doi:10.7498/aps.71.20211344
[6]	周玚, 任信钢, 闫业强, 任昊, 杜红梅, 蔡雪原, 黄志祥.基于双层电子传输层钙钛矿太阳能电池的物理机制. 必威体育下载 , 2022, 71(20): 208802.doi:10.7498/aps.71.20220725
[7]	王佩佩, 张晨曦, 胡李纳, 李仕奇, 任炜桦, 郝玉英.氧化镍在倒置平面钙钛矿太阳能电池中的应用进展. 必威体育下载 , 2021, 70(11): 118801.doi:10.7498/aps.70.20201896
[8]	王言博, 崔丹钰, 张才益, 韩礼元, 杨旭东.钙钛矿太阳能电池研究进展: 空间电势与光电转换机制. 必威体育下载 , 2019, 68(15): 158401.doi:10.7498/aps.68.20190569
[9]	王平, 郭立新, 杨银堂, 张志勇.铝氮共掺杂氧化锌纳米管电子结构的第一性原理研究. 必威体育下载 , 2013, 62(5): 056105.doi:10.7498/aps.62.056105
[10]	陈先梅, 王晓霞, 郜小勇, 赵显伟, 刘红涛, 张飒.掺银氧化锌纳米棒的水热法制备研究. 必威体育下载 , 2013, 62(5): 056104.doi:10.7498/aps.62.056104
[11]	陈超, 冀勇, 郜小勇, 赵孟珂, 马姣民, 张增院, 卢景霄.直流脉冲磁控反应溅射技术制备掺铝氧化锌薄膜的研究. 必威体育下载 , 2012, 61(3): 036104.doi:10.7498/aps.61.036104
[12]	李林娜, 陈新亮, 王斐, 孙建, 张德坤, 耿新华, 赵颖.H2 气对脉冲磁控溅射铝掺杂氧化锌薄膜性能的影响. 必威体育下载 , 2011, 60(6): 067304.doi:10.7498/aps.60.067304
[13]	张俊艳, 邓天松, 沈昕, 朱孔涛, 张琦锋, 吴锦雷.单根砷掺杂氧化锌纳米线场效应晶体管的电学及光学特性. 必威体育下载 , 2009, 58(6): 4156-4161.doi:10.7498/aps.58.4156
[14]	曹佳伟, 黄运华, 张跃, 廖庆亮, 邓战强.四针状纳米氧化锌电磁波吸收特性. 必威体育下载 , 2008, 57(6): 3641-3645.doi:10.7498/aps.57.3641
[15]	肖竞, 柏鑫, 张耿民.整齐排列的氧化锌纳米针阵列的场发射性能. 必威体育下载 , 2008, 57(11): 7057-7062.doi:10.7498/aps.57.7057
[16]	孙晖, 张琦锋, 吴锦雷.基于氧化锌纳米线的紫外发光二极管. 必威体育下载 , 2007, 56(6): 3479-3482.doi:10.7498/aps.56.3479
[17]	姚志涛, 孙新瑞, 许海军, 姜卫粉, 肖顺华, 李新建.氧化锌/硅纳米孔柱阵列的结构和光致发光特性研究. 必威体育下载 , 2007, 56(10): 6098-6103.doi:10.7498/aps.56.6098
[18]	邵光杰, 秦秀娟, 刘日平, 王文魁, 姚玉书.氧化锌纳米晶高压下的晶粒演化和性能. 必威体育下载 , 2006, 55(1): 472-476.doi:10.7498/aps.55.472
[19]	倪赛力, 常永勤, 龙毅, 叶荣昌.氧化锌纳米棒场发射性能研究. 必威体育下载 , 2006, 55(10): 5409-5412.doi:10.7498/aps.55.5409
[20]	辛显双, 周百斌, 吕树臣, 苏文辉.掺铕纳米氧化锌的制备及其发光性质. 必威体育下载 , 2005, 54(4): 1859-1862.doi:10.7498/aps.54.1859

计量

文章访问数:9110
PDF下载量:145
被引次数:0

搜索

留言板