Molten salt method is applied to synthesis stoichiometric nano-LiNiO2 in rather low temperature and short time. Our results indicate that in the process of preheating the better-crystallized LiNiO2 powder with better electrochemical performances can be produced. The final samples before and after preheating exhibit the initial discharge capacities of 151 and 148 mAh ·g-1 respectively. After 100 cycles, they decay to only 55 and 118 mAh ·g-1, with capacity retentions being 36.4% and 79.7% respectively. The lowered cation disordering is thought to be favorable for the diffusion of lithium ions, by which the enhanced electrochemial properties can be explained.